The mechanical behavior of the recently produced gas pipes material PE100 is investigated and compared to the commonly used material PE80 to determine their relative advantages. The two materials show plastic behavior at room temperature. The fracture toughness of the two materials is experimentally determined using the two common elastic plastic fracture mechanics methods: the American Society for Testing and Materials (ASTM) multiple specimen test method for determining the J-R curve of the materials, and the crack opening displacement method. The investigation of the fracture behavior of the two materials includes the effect of the specimen thickness as well as specimen configuration. The experimental tests were carried on the compact tension specimens and the single edge notch bending (SENB) specimens. At −70°C, the materials show elastic behavior, the ASTM test method for determining fracture toughness is applied to SENB specimens to determine KIC of both materials. PE80 shows greater resistance to fracture than PE100.

Keywords:
fracture toughness, polymers, pipes, plasticity, materials testing, integral equations, Polyethylene, J-Integral, Fracture Toughness, Crack Opening Displacement
Topics:
Fracture (Materials), Fracture toughness, Pipes, Mechanical properties, Displacement, Temperature
1.
Haung, D. D., 1991, “The Application of the Multispecimen J-Integral Technique to Toughened Polymers,” Elastic-Plastic Fracture Test Methods: The Users Experience (2nd volume), ASTM STP114, J. A. Toyce, ed., American Society for Testing and Materials, Philadelphia, pp. 290–305.
2.
Chung, W. N., and Williams, J. G., 1991, “Determination of JIC for Polymers Using the Single Specimen Method,” Elastic-Plastic Fracture Test Methods: The Useres Experience (2nd volume), ASTM STP114, J. A. Toyce, ed., American Society for Testing and Materials, Philadelphia, pp. 320–339.
3.
Che
,
M.
,
Grellmann
,
W.
, and
Seidler
,
S.
,
1997
, “
Crack Resistance Behavior of Polyvinylchloride
,”
J. Appl. Polym. Sci.
,
64
, pp.
1079
–
1090
.
4.
Hashemi
,
S.
, and
Williams
,
J. G.
,
1986
, “
A Fracture Toughness Study on Low Density and Linear Low Density Polyethylenes
,”
Polymer
,
27
, pp.
384
–
392
.
5.
Chan
,
M. K. V.
, and
Williams
,
J. G.
,
1983
, “
J-Integral Studies of Crack Initiation of a Tough High Density Polyethylenes
,”
Int. J. Fract.
,
19
, pp.
145
–
159
.
6.
Hashemi
,
S.
, and
Williams
,
J. G.
,
1986
, “
Fracture Characterization of Tough Polymers Using the J Method
,”
Polym. Eng. Sci.
,
26
(
11
), pp.
760
–
767
.
7.
Hashemi
,
S.
, and
Williams
,
J. G.
,
1986
, “
The Effects of Specimen Configuration and Notch Tip Radius on Fracture Toughness of Polymers Using JC,
”
Plast. Rubber Process. Applic.
,
6
(
4
), pp.
363
–
375
.
8.
Haung
,
D. D.
, and
Williams
,
J. G.
,
1987
, “
J Testing of Toughened Nylons
,”
J. Mater. Sci.
,
22
, pp.
2503
–
2508
.
9.
Darwish
,
A. Y.
,
Mandell
,
J. F.
, and
McGarry
,
F. J.
,
1982
, “
Plane Strain Fracture Toughness of Polyethylene Pipe Materials
,”
MIT Research Report
R82-2.
10.
Chan
,
M. K. V.
, and
Williams
,
J. G.
,
1981
, “
Plane Strain Fracture Toughness Testing of High Density Polyethylene
,”
Polym. Eng. Sci.
,
21
(
15
), pp.
1019
–
1026
.
11.
Mandell
,
J. F.
,
Roberts
,
D. R.
, and
McGarry
,
F. J.
,
1983
, “
Plane Strain Fracture Toughness of Polyethylene Pipe Materials
,”
Polym. Eng. Sci.
,
23
(
7
), pp.
401
–
411
.
12.
Flaieler, P., Roberts, D. R., Mandell, J. F., and McGarry, F. J., 1981, “Fracture Toughness Testing of HDPE Plastic Pipe,” Physical Testing of Plastics, ASTM STP150, pp. 15–31.
13.
Darwish
,
A. Y.
,
Mandell
,
J. F.
, and
McGarry
,
F. J.
,
1981
, “
Applicability of Linear Elastic Fracture Mechanics to Rigid PVC Pipe Materials
,”
MIT Research Report
R81-1.
14.
ASTM Standards, 1996, “Standard Test Method for Determining J-R Curves of Plastic Materials,” ASTM-D6068.
15.
ASTM Standards, 1989, “Standard Test Method for JIC, a Measure of Fracture Toughness,” ASTM-E813.
16.
ASTM Standards, 1993, “Standard Test Method for Crack Tip Opening Displacement (CTOD) Fracture Toughness Measurement,” ASTM-E1290.
17.
ASTM Standards, 1983, “Plane Strain Fracture Toughness of Metallic Materials,” ASTM-E399.
18.
British Standards, 1998, “Methods of Testing Plastics,” BS 2782.
19.
ASTM Standards, 1994, “Standard Test Method for Tensile Properties of Plastics,” ASTM D638-94b.
Copyright © 2005
 by ASME
You do not currently have access to this content.